Page 16 - ArtMolds Journal June-July 2103 Mod 4
P. 16
often omit these expensive options.  ture, and skim again just prior to pouring.  Further Reading  Another problem is that gas fired  Get the small size if you are starting out  For sand casting I would recommend  units tend to range in noise from  casting aluminum and intend to try anoth‐   two books. The first is the "Bible" by  C.W.  moderately loud to Saturn 5 imper‐ er metal later.  Ammen titled "The Complete Handbook of  sonations. The burning gas and com‐   Degassers: Using a degasser depends  bustion air expands in volume and  a lot on what you are going to do with the  Sand Casting". This book is very complete  creates jet engine sorts of sounds  metal, and the initial condition of the met‐ in all aspects of small foundry operation.  and impressive flame columns rising  al source. Degasser helps to eliminate gas  The second is a more basic book by Wil‐ liam A. Cannon titled "How to Cast Small  from the vent hole.  from the melt. If you have gas in the melt  Metal and Rubber Parts". This book is a    It comes down to what tempera‐ it may come out of solution at the sand /  tures you need. I would go with an  metal interface in the mold and leave sur‐ good introduction to casting simple, single  electric unit for aluminum or lower,  face bubbles and defects. Another prob‐ sided items such as plaques and belt buck‐ but a gas unit is a must for anything  lem with dissolved gas is internal voids  les. David Gingery has written an excellent  with a higher melting point.   and porosity. Items such as artwork that  series of books on building a machine shop    require a fine surface finish or structural  from scrap, using sand casting as the basis  for making the necessary parts. His books  Chemicals  machine parts will benefit from degassing.  are available from Lindsay Publications.     Parting Dust: Parting dust  The condition of the feed stock also plays    a big part. New metal of graded quality is  (release agent) is a fine powder used  Online resources   not as much of a problem as recycled met‐ to prevent the sand from sticking to    I'd suggest that you also check out the  the patterns. It is also used to pre‐ als. The big difference is the surface area  vent the cope sand from sticking to  of the feed stock. Scrap tends to have a  HFA Forum at Home Foundry Association.  the drag sand at the parting line of  large surface area per unit volume and is  There are a number of excellent links from  more likely to pick up gas during melting.  there. Also there is a mailing list called  the flask. Get a small box and use an  Get the small size degasser to start with.  hobbicast that you can sign up (free) that  old gym sock as the dusting bag.  links you to a bunch of people who are    Fluxes: I would recommend that    Tools: A lot of foundry men will make  you use a flux when melting your  some of the basic tools such as slicks  very knowledgeable on a wide variety of  metal at all times. A flux will help  (used for smoothing and patching dam‐ subjects. To learn more about the Gingery  aged sand areas) and sprue cutters (cuts a  style of furnace, check out Lindsay books.  separate the dross and slag impuri‐ funnel shaped opening in the sand thru  There you can find a lot of information  ties from the metal and also creates  about building furnaces. Lindsay also has  a floating layer that protects the  which molten metal is poured into the  melt from oxidation and absorbing  cavity) by bending up old teaspoons and  an extensive library of home foundry  hydrogen and other gasses. The  flatware to suit. If you are using green  books. Tell him I sent you! Check out this  (water bonded) sand you can find a camel  foundry page by Lionel Oliver. It has a lot  heavier contaminants such as steel  hair artists brush at art supply stores that  of good information and pictures to help  bits will sink, while the oxides will  you get started.  float to the top and can be skimmed  will work fine as a swab for slicking up the  off. I add about half the amount at  sand before / after pulling a pattern. I use  Paul Encoyand is the founder and CEO  the beginning of the melt. Then I  sections of hardwood clothes hanger rods  of Budget Casting Supply, located in  from the closet for sprue and riser  skim the surface after the metal has  patterns. Just cut a funnel shape on top  Sonora, California. He can reached at:  completely melted, and add the sec‐ ond half. Allow time for the material  after pulling the dowel material out of the  209‐694‐8601 /Email:  to super heat to pouring tempera‐ sand.   [email protected]  BUDGET CASTING SUPPLY LLC Supplies for the Small Commercial and Hobby Foundry  PARTING DUST & MOLD RELEASE  ALUMINUM CASTING  FOUNDRY SAND  BRASS CASTING  CORE BINDER  IRON CASTING  REFRACTORY MATERIALS  FURNACE COMPONENTS  PATTERN LETTERS & TOOLS  SAFETY EQUIPMENT  CRUCIBLES, TONGS & FLASKS  MATERIALS 20811 Upper Hillview Drive : Sonora, CA 95370  : T. 209‐694‐8601  : Email: [email protected]   June | July 2013 ARTMOLDS JOURNAL | 16 
   11   12   13   14   15   16   17   18   19   20   21